Hard alloy on chemical vapor deposition (CVD) diamond film coating have shown excellent tool for industrial application. However, the biggest technical obstacle to the application of such tool materials is the low bonding strength between the deposited diamond film and the cemented carbide substrate. The main reasons are: 1 There is a difference between the coefficients of thermal expansion (WC has a coefficient of thermal expansion of 4 × 10 -6 to 6.2 × 10 -6 / ° C, and the coefficient of thermal expansion of diamond is 1.2 × 10 -6 to 4.5 × 10 -6 / ° C). The solubility of 2C in the matrix Co is large. The diffusion coefficient of 3C in the matrix Co is high. The latter two factors promote the growth of graphite under CVD diamond conditions, interfering with the nucleation and growth of diamond, resulting in limited diamond nucleation and graphite deposition. If there is enough diamond nucleation, a continuous diamond film is formed, but because of the non-adherent graphite phase between the matrix and the diamond film, the interface is destroyed and the diamond film is always peeled off from the substrate. The reaction between Co in the surface of the substrate and C in the deposition gas source is the biggest technical obstacle to the adhesion of the diamond film to the cemented carbide tool. The key to enhancing adhesion is to remove Co from the surface of the substrate or inhibit its activity or motility. A common way to solve this problem is to reduce the amount of Co contained in the entire tool or apply an intermediate layer on the surface of the tool. However, the Co combined phase provides strength to the tool, and the overall reduction of the Co content of the tool will affect the performance of the cutting performance. The application of a suitable intermediate layer between the substrate and the diamond film can significantly improve the bonding properties therebetween. Figure 1 Diamond film deposited on a carbon-free carbide substrate [next] 1. Surface de-Co treatment When chemically vapor-depositing a diamond film on a cemented carbide substrate, it is necessary to remove Co from the surface because Co is not conducive to the deposition of the diamond film. KUNIO SHIBUKI pointed out that the size of the pores generated on the surface of Co from the WC-Co substrate surface has a certain influence on the adhesion strength of the diamond film. When the hole size and the diamond particle size are almost the same, the adhesion strength of the diamond film is the best, and the flank wear of the diamond film cemented carbide insert is extremely small when the Al-10%Si alloy is cut. 3 Apply a transition layer [next] 4 Outlook [next] In the simplest of terms, an Overhead Crane is a machine, or piece of equipment, that allows you to lift and move heavy materials from one location to another in a precise manner.Eurocrane overhead crane adopts European concept ,has the features of superior performance,compact structure,small dimension of headroom and makingfull use of available space of the plant. In addition the design of the product has fully considered the requirements of customers to increase the safety and easiness during the use. The standard configuration includes trolley frequency conversion and cart frequency conversion to make the running stable and reliable. Single Girder Overhead Crane,Single Girder Overhead Travelling Crane,Single Girder Overhead Bridge Crane,Single Girder Top Running Crane,EOT Crane,Single Girder Electric Overhead Traveling Crane Eurocrane (China) Co., Ltd. , https://www.craneparts.pl
This paper reviews various current studies in improving the bond strength between diamond films and cemented carbide substrates, including the preparation of fine-grained substrates, pre-treatment of substrates, optimization of process conditions for CVD diamond films, and in substrates and diamond films. The transition layer is applied between them, and the research prospects of depositing diamond film on cemented carbide are discussed in order to lay a foundation for the application of diamond film cutter.
1 Matrix material and its pretreatment 1. Matrix material KUNIO SHIBUKI pointed out that the WC particle size in WC-Co has a certain influence on diamond nucleation. Diamond is easy to deposit at the WC particle boundary. The finer the WC particle is, the smaller the size is. The higher the nucleation density of the diamond, the better the adhesion of the diamond film. 32 When the WC particle size is about 1 μm, the nucleation density of the diamond film is 9 × 10 6 cm -2 , and when the WC particle size is about 0.5 μm, the nucleation density of the diamond film is 5 × 10 7 cm - 2 . 
After etching the substrate for 10 min with a nitric acid solution (HNO 3 : H 2 O = 1:1), the amount of Co on the surface of the substrate was decreased by 0.2% [9] . MATaher grinds the WC-6%Co and WC-22%Co substrates with 1500 mesh diamond paper and then chemically etches them in a nitric acid solution (HNO 3 :H 2 O=1:3) for 10 min to remove Co on the surface of the substrate. The substrate is then ultrasonically treated (diamond particles size less than 0.1 μm for 3 min) [10] . The energy scattering spectrum (EDS) test results show that the surface contains less than 1% Co. For a substrate having a Co content of less than 1% on the surface, Co has no effect on the nucleation and growth of the diamond, and the nucleation density of the diamond is about 108 cm -2 . It is also pointed out that in order to obtain a higher adhesion strength of the diamond film, the roughness of the surface of the substrate should be in a certain range (Ra = 0.06 ~ 0.25 μm).
IO.SAITO pointed out that the Co on the surface of WC-Co is selectively etched by 2.5% CO-H 2 plasma, and the diamond film prepared at a Co concentration of 10% has the best properties, and its adhesion strength is 1.7 kgfmm. -2 , Vickers hardness is 8500kgfmm -2 . M. MURAKAWA et al. sputtered Co on the surface of WC-Co with Ar ion to reduce the content of Co to 0.8%, because the sputtering rate of Ar ion to Co and WC differed a lot, and the ratio of sputtering rate It is about 5:1.
Li Chengming et al. used excimer laser irradiation pretreatment on cemented carbide substrates, using the large difference in the melting point of Co and WC (WC melting point is 2800 ° C, Co melting point is 1495 ° C), the selectivity generated by high energy laser beam Evaporation removes the Co of the surface layer of the YG6 cemented carbide, and the surface of the cemented carbide is roughened by laser surface modification, thereby causing a pinning effect on the diamond film, thereby further enhancing the bonding strength between the diamond film and the substrate.
1. Surface de-C treatment For the hot-pressed WC substrate, first remove the carbon with 2% O 2 -H 2 plasma, then coarsen the surface with diamond particles, and finally deposit the diamond film by MWPCVD, as shown in Figure 1. Shown. 2% O 2 -H 2 plasma etches the surface of the WC substrate, so that WC goes to C as W, and W is completely carbonized during diamond deposition, producing extremely fine WC particles (having a size of about 10 to 100 nm). Among them, the decarburization of WC and the carbonization process of W play an important role in the improvement of the adhesion strength of the diamond film due to an increase in the contact area between the diamond film and the extremely fine WC particles. As can be seen from Figure 1, the fine WC particles of the matrix invade into the diamond film. The adhesion of the diamond film is enhanced by the wedge effect of invading the WC particles.
2 Process conditions of CVD diamond film 1. Gas source type and gas concentration [next]
MA Taher et al. studied the deposition of diamond films with varying concentrations of CH 4 (1%, 3%, 5%, 7%, 9%). The results show that there is a certain relationship between the grain size of the deposited diamond film and the concentration of CH 4 . When the concentration of CH4 is 0.5% to 1%, the grain size of diamond is 5-11 μm; when the concentration of CH 4 is 1% to 4%. The diamond grain size is 11 to 60 μm. The diamond film cemented carbide insert deposited at the CH 4 concentration of 3% has the best mechanical properties.
IO.SAITO et al. studied the effect of CO concentration on diamond film deposition. It is pointed out that the diamond film prepared at a CO concentration of 10% has the best properties, and its adhesion strength is 1.7kgfmm -2 and Vickers hardness is 8500kgfmm - 2 . The adhesion strength of the diamond film prepared at a CO concentration of 5% is 0.5 kgfmm -2 and the Vickers hardness is 10000 kgfmm -2 ; the adhesion strength of the prepared diamond film is 2.5 kgfmm -2 when the CO concentration is 50%. The hardness is 4000kgfmm -2 .
M. MURAKAWA et al. pointed out that by using HFCVD method and using ethanol as a carbon source, a good quality diamond film layer can be obtained on a Co-rich WC alloy without special pretreatment of the cemented carbide substrate. Further, when the diamond film cutter for cutting the order of 2.5mm thick aluminum plate, punching after 5 × 10 4, the cutter head No sharp abrasive grains of diamond film and the debris cut adhesion material The phenomenon of adhesion.
1. Deposition temperature KUNIO SHIBUKI et al. pointed out that the adhesion strength of diamond film increases with the increase of deposition temperature. The results are shown in Table 1. When cutting Al-10%Si alloy, the flank wear of the diamond film cemented carbide insert is extremely small.
An intermediate layer is deposited between the WC-Co and the diamond film, and the intermediate layer is used as a diffusion barrier layer of C or Co, thereby solving the problem that the bonding strength between the deposited diamond film and the cemented carbide substrate is too low. The interfacial stress and film stress may be compensated for due to the difference in thermal expansion coefficient between the intermediate layer and the diamond film. A previous study was to deposit a compound of Si as an intermediate layer of diamond deposited on WC-Co. A diamond multilayer film structure developed by JM Albella et al. on a cemented carbide substrate is WC-8% Co/B/TiB 2 /B/diamond, wherein the total thickness of B/TiB 2 /B is less than 1 μm (thin B layer, 0.6μm TiB 2 , thin B layer), the best adhesion of the diamond film. The purpose of each part of the intermediate layer is different: 1 The initial B layer reacts with the Co on the surface of the cemented carbide tool to form Co 2 B and CoB. Therefore, the deposited first layer B is an effective measure for reducing the activity and mobility of Co on the surface of the cemented carbide tool. ② Then, on the first layer deposited on a B or a boron nitride layer of TiB 2. For TiB 2 , CoB is thermodynamically stable, and the absence of B on the surface of the substrate enhances the bond between Co 2 B and CoB 2 and TiB 2 . The role of TiB 2 is to act as a diffusion barrier layer to separate C and Co. 3 The final layer B enhances the adhesion of diamond to TiB 2 . There are more chemical reactions between B and TiB 2 and B and diamond than between TiB 2 and diamond. Further, since B is deposited in an amorphous form, it can be used as a stress absorber. It is also noted herein that single layer B or single layer TiB 2 is effective in increasing diamond nucleation density, but does not improve adhesion of the diamond film.
JM Albella et al. developed another multilayer film structure for improving the bonding strength between diamond film and cemented carbide substrate. The process has three steps: 1 CVD layer of discontinuous diamond core; 2 electrodeposition of a layer of Ni, Fix the diamond core deposited on the substrate first, and fill the entire gap of the diamond with Ni; 3 CVD diamond film; its structure is shown in Figure 2.
Research on improving the adhesion strength of diamond films on cemented carbides focuses on the following aspects: 1 Select a suitable matrix material. 2 The pretreatment of the surface of the substrate concentrates on the decarburization and decarburization treatment of the crystal seeds and the substrate which are sprayed with a diamond-like structure on the surface. 3 Optimize the film forming process conditions. 4 Apply a transition layer between the substrate and the diamond film. These aspects are effective to improve the adhesion strength of the diamond film to a certain extent, but so far, no fundamental solution has been found. A lot of work has been done on the first three aspects of research, but studies on the transition layer to improve the bonding properties between the matrix and the diamond film have just begun. Considering that the chemical vapor deposition (CVD) diamond film on the tool substrate has a low adhesion strength, and the bonding property between the metal Mo and the diamond film is good, the author proposes to adopt a multilayer film structure, that is, a cemented carbide substrate/Ni- Mo electrodeposited layer/Ni-Mo-diamond particles (having a particle size of about several micrometers) composite electrodeposited layer/chemical vapor deposited diamond film. A Ni-Mo deposited layer and a Ni-Mo-diamond composite electrodeposited layer are introduced as an intermediate layer between the diamond film and the cemented carbide substrate to improve the bonding property therebetween. Because of the deposition layer containing Mo, the nucleation density of diamond on the surface of the substrate can be greatly improved, and the addition of diamond particles can obtain several homoepitaxial growth microdomains on the surface of the substrate, thereby improving the bonding strength therebetween. Currently, this research is ongoing.